The Effectiveness of the Addition of Silicone Dioxide Nanoparticles (SiO2) to the Flexural Strength and Surface Hardness of the Base of Heat Polymerization Resin Denture (RAPP): Systematic Study

Introduction

Complete dentures play a crucial role in replacing missing teeth and providing adequate support and retention to the upper and lower jaws. One of the primary materials used to fabricate the base of dentures is heat polymerization acrylic resin (RAPP). Although RAPP offers several advantages, including aesthetics, ease of manipulation, and non-toxicity, its flexural strength and surface hardness are relatively low, making it vulnerable to breakage. The addition of reinforcement materials, such as nanoparticles silicon dioxide (SiO2), is expected to improve these characteristics.

Background

Heat polymerization acrylic resin (RAPP) is a widely used material in dentistry due to its ease of manipulation, non-toxicity, and aesthetic appeal. However, its flexural strength and surface hardness are relatively low, making it prone to breakage. The addition of reinforcement materials, such as nanoparticles silicon dioxide (SiO2), has been proposed as a potential solution to improve the mechanical properties of RAPP. SiO2 nanoparticles have been shown to enhance the flexural strength and surface hardness of various materials, including polymers and ceramics.

Purpose of the Study

The purpose of this systematic study is to analyze the effectiveness of the addition of silicone dioxide nanoparticles (SiO2) to the flexural strength and surface hardness of the base of heat polymerization resin denture (RAPP). This study aims to provide a comprehensive review of the existing literature on the use of SiO2 nanoparticles in RAPP and to identify the optimal concentration of SiO2 that can improve the mechanical properties of RAPP.

Methodology

This systematic study was conducted using the prism method as a guide for selecting relevant journals. The database used as a source was Pubmed and Google Scholar, with searches conducted using keywords in the Boolean, Picos, as well as predetermined inclusion and exclusion criteria. To eliminate duplicated journals, the Mendeley application was used as a citation manager. Each stage of this systematic study was well recorded to ensure transparency in the research process.

Results

A total of 5 qualified journals were selected for examination, published between 2012 and 2022. The results of the analysis showed that one journal concluded that there was an increase in flexural and surface hardness in the RAPP denture base with a concentration of nanoparticles SiO2 by 3%, 5%, and 7%. Three other journals showed an increase in concentrations of 1% and 5%. However, there was one journal that reported a decrease in effectiveness at a concentration of 3%, 5%, and 7%.

Discussion

Based on the information obtained from the selected journals, it can be concluded that the concentration of silicone dioxide nanoparticles is 1%, 3%, and 7% produces relatively low flexural strength and surface hardness on the base of RAPP artificial dentures. Meanwhile, a concentration of 5% SiO2 shows the most significant increase in flexural and surface hardness. This confirms that the selection of the right nanoparticles concentration is very crucial to improve the mechanical properties of the material.

Conclusion

The results of this systematic study suggest that the addition of silicone dioxide nanoparticles (SiO2) can improve the flexural strength and surface hardness of the base of heat polymerization resin denture (RAPP). The optimal concentration of SiO2 that can achieve this improvement is 5%. This study highlights the importance of considering the use of SiO2 nanoparticles in the development of denture materials. With the right use, this nanoparticles can significantly increase the strength and durability of artificial dentures, thus providing long-term benefits for patients. Further research is also needed to understand the mechanisms that underlie this mechanical properties and to explore other combinations of nanoparticles that can improve the performance of artificial dental base materials.

Recommendations

Based on the findings of this systematic study, the following recommendations are made:

Use of SiO2 nanoparticles: The use of SiO2 nanoparticles in the development of denture materials is recommended to improve the mechanical properties of RAPP.
Optimal concentration: The optimal concentration of SiO2 that can achieve this improvement is 5%.
Further research: Further research is needed to understand the mechanisms that underlie this mechanical properties and to explore other combinations of nanoparticles that can improve the performance of artificial dental base materials.

Limitations

This systematic study has several limitations, including:

Limited number of journals: The number of journals selected for examination was limited, which may have affected the generalizability of the findings.
Variability in concentrations: The concentrations of SiO2 used in the selected journals varied, which may have affected the results.
Lack of control group: The lack of a control group in some of the selected journals may have affected the validity of the findings.

Future Directions

Future studies should aim to:

Investigate the mechanisms: Investigate the mechanisms that underlie the improvement in mechanical properties of RAPP with the addition of SiO2 nanoparticles.
Explore other combinations: Explore other combinations of nanoparticles that can improve the performance of artificial dental base materials.
Conduct in vitro and in vivo studies: Conduct in vitro and in vivo studies to evaluate the efficacy and safety of SiO2 nanoparticles in RAPP.
Q&A: The Effectiveness of the Addition of Silicone Dioxide Nanoparticles (SiO2) to the Flexural Strength and Surface Hardness of the Base of Heat Polymerization Resin Denture (RAPP)

Frequently Asked Questions

Q: What is the purpose of this study?

A: The purpose of this study is to analyze the effectiveness of the addition of silicone dioxide nanoparticles (SiO2) to the flexural strength and surface hardness of the base of heat polymerization resin denture (RAPP).

Q: What are the benefits of using SiO2 nanoparticles in RAPP?

A: The addition of SiO2 nanoparticles can improve the flexural strength and surface hardness of RAPP, making it more durable and resistant to breakage.

Q: What is the optimal concentration of SiO2 that can achieve this improvement?

A: The optimal concentration of SiO2 that can achieve this improvement is 5%.

Q: How does the addition of SiO2 nanoparticles affect the mechanical properties of RAPP?

A: The addition of SiO2 nanoparticles can improve the flexural strength and surface hardness of RAPP, making it more resistant to breakage and wear.

Q: What are the limitations of this study?

A: The limitations of this study include the limited number of journals selected for examination, the variability in concentrations of SiO2 used, and the lack of a control group in some of the selected journals.

Q: What are the future directions for this research?

A: Future studies should aim to investigate the mechanisms that underlie the improvement in mechanical properties of RAPP with the addition of SiO2 nanoparticles, explore other combinations of nanoparticles that can improve the performance of artificial dental base materials, and conduct in vitro and in vivo studies to evaluate the efficacy and safety of SiO2 nanoparticles in RAPP.

Q: What are the implications of this study for dentistry?

A: The findings of this study suggest that the addition of SiO2 nanoparticles can improve the mechanical properties of RAPP, making it a more durable and resistant material for denture fabrication. This has implications for the development of more effective and long-lasting dentures.

Q: What are the potential applications of this research?

A: The potential applications of this research include the development of more effective and long-lasting dentures, the improvement of dental implant materials, and the creation of new biomaterials for dental applications.

Q: What are the next steps for this research?

A: The next steps for this research include conducting further studies to investigate the mechanisms that underlie the improvement in mechanical properties of RAPP with the addition of SiO2 nanoparticles, exploring other combinations of nanoparticles that can improve the performance of artificial dental base materials, and conducting in vitro and in vivo studies to evaluate the efficacy and safety of SiO2 nanoparticles in RAPP.

Q: How can this research be applied in a clinical setting?

A: The findings of this study can be applied in a clinical setting by using SiO2 nanoparticles in the fabrication of dentures, which can improve the mechanical properties of RAPP and make it a more durable and resistant material for denture fabrication.

Q: What are the potential risks and benefits of using SiO2 nanoparticles in RAPP?

A: The potential risks and benefits of using SiO2 nanoparticles in RAPP include the potential for improved mechanical properties, reduced wear and tear, and increased durability, as well as the potential for adverse reactions or toxicity.

Q: How can the findings of this study be used to improve dental care?

A: The findings of this study can be used to improve dental care by developing more effective and long-lasting dentures, improving the mechanical properties of RAPP, and creating new biomaterials for dental applications.